Para-equilibrium Phase Diagram

Purpose: Learn to perform phase diagram calculations in para-equilibrium condition with fast diffusion elements.

Module: PanPhaseDiagram

Thermodynamic Database: FeNiC.tdb

Batch file: Example_#1.27.pbfx

Background: In certain systems, some interstitial elements, such as C and N, diffuse much faster than others. Therefore, those elements can be treated as “mobile” components, while the others are treated as immobile components. The common case is the austenite to ferrite reaction in steels by a rapid carbon-diffusion controlled process.

Calculation Procedures:

Load FeNiC.tdb following the procedure in Pandat User's Guide: Load Database ;
Perform a Section Calculation from PanPhaseDiagram, and set the calculation condition as shown in Figure 1;
Click “Mobile Comps.”, set “C” the mobile component as shown in Figure 2;
After properly selected the C as mobile component, then click OK, it returns to the calculation condition window as shown in Figure 3. The mobile element highlighted with orange color.

Figure 1: Normal 2D calculation of an isotherm of Fe-Ni-C at 1000 K

Figure 2: Set mobile components

Figure 3: Calculation condition of para-equilibrium isothermal section of Fe-Ni-C at 1000 K

Post Calculation Operation:

Add tie-lines and change graph appearance following the procedure in Pandat User's Guide: Property;
Label the graph following the procedure in Pandat User's Guide: Icons for Graph on Toolbar;
The Para-equilibrium isothermal section is shown as Figure 4

Figure 4: Calculated para-equilibrium isothermal section of Fe-Ni-C at 1000 K